Abstract
Due to the intricate and volatile nature of the service environment surrounding prestressing anchoring materials, stress corrosion poses a significant challenge to the sustained stability of underground reinforcement systems. Consequently, it is imperative to identify effective countermeasures against stress corrosion failure in cable bolts within deep underground environments, thereby ensuring the safety of deep resource extraction processes. In this study, the influence of various coatings on the stress corrosion resistance of cable bolts was meticulously examined and evaluated using specifically designed stress-corrosion-testing systems. The specimens were subjected to loading using four-point bending frames and exposed to simulated underground corrosive environments. A detailed analysis and comparison of the failure patterns and mechanisms of specimens coated with different materials were conducted through the meticulous observation of fractographic features. The results revealed stark differences in the stress corrosion behavior of coated and uncoated bolts. Notably, epoxy coatings and chlorinated rubber coatings exhibited superior anti-corrosion capabilities. Conversely, galvanized layers demonstrated the weakest effect due to their sacrificial anti-corrosion mechanism. Furthermore, the effectiveness of the coatings was found to be closely linked to the curing agent and additives used. The findings provide valuable insights for the design and selection of coatings that can enhance the durability and reliability of cable bolts in deep underground environments.