Abstract
The strong hygroscopicity of wood greatly shortens its service life. Here, a simple impregnation modification approach was used to construct superhydrophobic silicone resin coatings on wood surfaces. Briefly, with hydrofluorosilicone oil (HFSO), tetramethyl tetravinyl cyclotetrasiloxane (V(4)), and hydrophobic SiO(2) from industrial production as raw materials, superhydrophobic wood samples (water contact angle ~160.8°, sliding angle ~3.6°) can be obtained by simply dipping the wood in the HFSO/V(4)/SiO(2) modifier solutions. As a result, the superhydrophobic silicone resin coating constructed on the wood surface still has good water repellency after finger touching, tape peeling, and sandpaper abrasion. When the mass ratio of HFSO to V(4) is 2:1, the water absorption of the resulting wood after soaking in water for 24 h is only 29.2%. Further, the resulting superhydrophobic wood shows excellent anti-fouling properties. Finally, we believe that the impregnation modification method proposed in this study can be applied to the protection of cellulose substrates.