Abstract
In this work, a novel zinc-aluminum-magnesium (Zn-Al-Mg, ZM) coated steel was prepared using the hot-dip method. The microstructure and corrosion resistance of the ZM-coated steel were investigated. Compared to the conventional galvanized steel (GI), the ZM coating demonstrated a distinctive phase structure, consisting of Zn phase, binary eutectic (Zn/MgZn(2)), and ternary eutectic (Zn/Al/MgZn(2)). The corrosion resistance of the ZM-coated and GI-coated steels was evaluated by neutral salt spray test (NSST), polarization and electrochemical impedance spectroscopy (EIS). The results indicated that ZM-coated steel provided superior long-term corrosion protection in a NaCl environment compared to GI-coated steel. The scanning vibrating electrode technique (SVET) proved to be an effective method for investigating the evolution of the anodic and cathodic on the local coating surface. GI-coated steel exhibited a potential and current density distribution between the cathodic and anodic sites nearly three orders of magnitude higher than that of ZM-coated steel, suggesting a higher corrosion rate for GI-coated steel.