Abstract
In this study, Fe(60)Co(10-x)Ni(15)Cr(15)Si(x) (x = 0, 4, and 8) powders were successfully prepared using the aerosol method and employed to produce high-entropy coatings on Q235 steel via laser cladding. The microstructure and phase composition of the coatings were analyzed using scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction. Corrosion resistance and potential were evaluated through electrochemical analysis and Kelvin probe force microscopy. The results show that the Fe(60)Co(10-x)Ni(15)Cr(15)Si(x) coatings exhibit excellent metallurgical bonding with no visible porosity or cracks. The coating primarily consists of an FCC structure; however, as the Si content increases, the structure transitions to a mixed FCC + BCC phase. The addition of Si also refines the grain size in the alloy system. Electrochemical analysis reveals that the Si0 and Si4 coatings exhibit similar corrosion behavior, while the Si8 coating shows a significant drop in corrosion potential, reducing its corrosion resistance. As the Si content increases, grain refinement leads to more grain boundaries, but the corrosion resistance decreases due to the lower corrosion performance of Si compared to Co. Considering both cost and corrosion resistance, the Si4 coating offers a balance of low cost and excellent corrosion resistance.