Abstract
This work studies the fabrication of CoCrFeNiMo high-entropy alloy (HEA) coatings via coaxial powder-fed laser cladding, addressing porosity and impurity issues in conventional methods. The HEA coatings exhibited eutectic/hypereutectic microstructures under all laser power conditions. A systematic investigation of laser power effects (1750-2500 W) reveals that 2250 W optimizes microstructure and performance, yielding a dual-phase structure with FCC matrix and dispersed σ phases (Fe-Cr/Mo-rich). The coating achieves exceptional hardness (738.3 HV(0.2), 3.8× substrate), ultralow wear rate (4.55 × 10(-5) mm(3)/N·m), and minimized corrosion current (2.31 × 10(-4) A/cm(2)) in 3.5 wt.% NaCl. The friction mechanism of the CoCrFeNiMo HEA coating is that in high-speed friction and wear, the oxide film is formed on the surface of the coating, and then the rupture of the oxide film leads to adhesive wear and abrasive wear. The corrosion mechanism is the galvanic corrosion caused by the potential difference between the FCC phase and the σ phase.