Abstract
It is important to improve the liquid lead corrosion resistance of fuel cladding alloy for promoting the development of lead-based reactors. The corrosion behaviors of traditional T91 steel and similar oxide dispersion strengthen ODS-type steels with or without the addition of Al, and were examined and compared at 600 °C in static oxygen-controlled liquid Pb in this research. High-temperature liquid lead corrosion tests were carried out for 120 h, 240 h, 500 h, 1000 h, and 2000 h, respectively, for three prepared samples. After the experiment, the corrosion behavior was evaluated and compared mainly based on the aspects of appearance, corrosion depth, microstructure, and composition difference. It was found that just the ODS design did not show a positive effect on corrosion resistance, while the addition of Al is beneficial to improving the corrosion resistance of ODS steel. The maximum corrosion depth of 9CrAl ODS is only 51.8 μm after corrosion for 2000 h, which is much lower than that of 9Cr-ODS steel. A thin film containing Al/Cr formed in the corrosion area after adding Al in 9Cr ODS steel, which played a positive role in corrosion resistance.