Abstract
The progress in tribocorrosion performance of the engineering parts is in dire need of improving their surface properties. In the present contribution, Ni-Cr-ZrO(2) layers were electrodeposited on St37 steel. The stress was put on optimizing the process factors, including the parameters involved in pulsed current electrodeposition and level of the ZrO(2) reinforcing nanoparticles (0-20 g/L) in the bath. The surface characteristics of the electrodeposits were evaluated using FESEM, EDS, AFM, and XRD. The tribomechanical characteristics of the films were determined using a Vickers microhardness tester and pin-on-disk apparatus. The electrochemical behavior of the samples was studied using OCP, EIS, PDP, and immersion techniques. The results demonstrated that the included ZrO(2) nanoparticles led to more homogenous, rougher, and defect-free surfaces, while they did not change the phase composition of the alloy electrodeposits. The polarization resistance of the Ni-Cr alloy coating increases by 6.7 times when 10 g/L of the reinforcing nanoparticles is added to the electrolyte. A decrease of ≈42 % in the mean COF value was obtained by the incorporation of 10 g/L ZrO(2) nanoparticles into the plating bath. The coating system developed holds the promise to address both technical requirements and health concerns.