Abstract
This study presents an eco-friendly approach for constructing superhydrophobic (S.H.) coatings on steel surfaces. The biо Сu nanoparticles are synthesized using a biоgenic process. Two types of coatings, Ni-Ѕ.Α and Ni-biо Сu-Ѕ.Α, were developed and characterized. The EDX results confirm the successful fabrication of two distinct coatings on the steel substrate: one involving the modification of nickel with stearic acid, Ni-Ѕ.Α, and the other involving the modification of nickel with both bio-Cu and stearic acid, Ni-biо Сu-Ѕ.Α. The SEM results revealed that the S.H. coats exhibit circular microstructures which contribute to the surface roughness. The contact angles of water droplets on the Ni-Ѕ.Α and Ni-biо Сu-Ѕ.Α coatings were measured at 158° ± 0.9° and 162° ± 1.1°, respectively. Chemical stability tests demonstrated that the Ni-Ѕ.Α coating maintains its S.H. behaviour in a pH range of 3-11, whereas the Ni-biо Сu-Ѕ.Α coating exhibits excellent chemical stability in a broader range of pH (1-13). The coating's mechanical stability was evaluated through abrasion tests. The Ni-Ѕ.Α coating retained its S.H. properties even after an abrasion length equal 1100 mm, while the Ni-biо Сu-Ѕ.Α coating maintained its S.H. behaviour till an abrasion length equal 1900 mm. The corrosion behavior and protective properties of the S.H. coatings were studied via electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PDP) techniques. The PDP and EIS findings demonstrated that both Ni-Ѕ.Α and Ni-biо Сu-Ѕ.Α coatings significantly reduced the corrosion rate compared to uncoated steel.