Abstract
In this study, the inhibitive performance of pyridine-2-thiol added to a corrosive solution was investigated for brass using potentiodynamic polarization, electrochemical impedance spectroscopy, and X-ray photoelectron spectroscopy. Electrochemical experiments were performed with different inhibitor concentrations in 0.5 M H(2)SO(4) as the corrosive medium. For potentiodynamic polarization, i(corr) values decreased significantly for the inhibited solutions in contrast with the uninhibited solution. Pyridine-2-thiol had an optimum inhibition concentration of 0.25 mM, giving an i(corr) value of 1.8 µA/cm(2) compared to 26 µA/cm(2) for the blank solution. EIS data indicated that R(p) and R(ct) values increased substantially after the addition of the corrosion inhibitor and corrosion inhibition efficiencies of more than 85% was achieved for the majority of the inhibited solutions. Scanning electron microscopy showed defect free and less scale formation for the inhibited surface but the bare brass surface had larger amounts of scale formation. X-ray photoelectron spectroscopy and UV-vis spectroscopy was used to investigate surface chemical composition and inhibitor structural changes over time.