Abstract
Herein, xylan-g-PMMA was synthesized by grafting poly(methyl methacrylate) (PMMA) onto xylan and characterized by FT-IR and HSQC NMR spectroscopies, and the xylan-g-PMMA/TiO(2) solution was used to electrospun nanofibers at the voltage of 15 Kv, which was the first time employing xylan to electrospun nanofibers. Moreover, the electrospinning operating parameters were optimized by assessing the electrospinning process and the morphology of electrospun fibers, as follows: the mixed solvent of DMF and chloroform in a volume ratio of 5:1, an anhydroxylose unit (AXU)/MMA molar ratio lower than 1:2, the flow speed of 0.00565-0.02260 mL/min, and a receiving distance of 10-15 cm. Diameters of the electrospun fibers increased with increasing DMF content in the used solvent mixture, MMA dosage, and receiving distance. TiO(2) nanoparticles were successfully dispersed in electrospun xylan-g-PMMA nanofibers and characterized by scanning electron microscopy, energy dispersive X-ray diffraction spectrum, and X-ray photoelectron spectroscopy, and their application for methylene blue (MB) degradation presented above 80% photocatalytic efficiency, showing the good potential in water treatment.