Abstract
Two polymerizable ionic liquids (or monomeric ionic liquids, mILs) namely 1-butyl-3-methylimidazolium and choline acrylates ([C4mim]A and ChA, respectively) were synthesized using the modified Fukumoto method from corresponding chlorides. The chemical structure of the prepared mILs was confirmed with FTIR and NMR study. Investigation of the thermal properties with DSC demonstrates that both mILs have a Tg temperature of about 180 K and a melting point around 310 K. It was shown that the temperature dependence of FTIR confirm the Tg to be below 200. Both mILs exhibited non-Newtonian shear thinning rheological behavior at shear rates >4 s−1. It was shown that [C4mim]A is able to dissolve bacterial cellulose (BC) leading to a decrease in its degree of polymerization and recrystallisation upon regeneration with water; although in the ChA, the crystalline structure and nanofibrous morphology of BC was preserved. It was demonstrated that the thixotropic and rheological properties of cellulose dispersion in ChA at room temperature makes this system a prospective ink for 3D printing with subsequent UV-curing. The 3D printed filaments based on ChA, containing 2 wt% of BC, and 1% of N,N′-methylenebisacrylamide after radical polymerization induced with 1% 2-hydroxy-2-methylpropiophenone, demonstrated Young’s modulus 7.1 ± 1.0 MPa with 1.2 ± 0.1 MPa and 40 ± 5% of strength and ultimate elongation, respectively.