Abstract
Polytetrafluoroethylene (PTFE) is widely used across various industrial and technological fields, including aerospace, automotive, electronics, and chemical processing. This work presents a sustainable approach to reusing PTFE waste and enhancing the limited applications of PTFE, which are constrained by its inferior mechanical properties, thermal expansion, and wear resistance. The reuse of PTFE scrap produced by lathe shops improves its previously mentioned properties by adding high-strength and high-stability ceramics. In this context, powder metallurgy technology produces PTFE-based composites reinforced with boron carbide (B(4)C) nanoparticles and graphene nanosheets. The phase composition and microstructure were determined using X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) techniques. XRD indicated the presence of PTFE and B(4)C phases in the chart of the specimens and the absence of graphene nanosheets due to their small quantity. The hybrid composite PTFE/5vol.% B(4)C/1 vol% graphene (GB6) recorded an increase in the microhardness, compressive stress, and Young’s modulus of 138.55%, 114.86%, and 78.70%, respectively, relative to the PTFE matrix (GB0). The results also indicated that the addition of reinforcements led to a significant improvement in wear resistance and thermal stability, with the GB6 sample recording a decrease in wear rate, coefficient of friction, and thermal expansion coefficient (CTE) value of 40.73%, 42.49%, and 57.94%, respectively, compared to the CB0 sample. Moreover, the addition of reinforcements to the PTFE matrix has the positive effect of increasing the electrical conductivity.