Abstract
To enhance the operational damage resistance of hydraulic machinery, this study employed laser cladding technology to fabricate a Co(37.4)Cr(30)Ni(20)Al(5)Ti(5)Nb(2.6) high-entropy alloy coating on 04Cr13Ni5Mo substrate. The influence of laser power on the microstructure and properties of the coating was systematically investigated. Based on preliminary research, the friction-wear performance and cavitation erosion behavior of the coatings prepared at 3000 W, 3200 W, and 3400 W were specifically examined. Results indicate that as the laser power increased from 3000 W to 3400 W, the microhardness of the coating gradually decreased from 345.3 HV(0.2). At 3000 W, the precipitation of trace strengthening phases significantly enhanced the mechanical properties. In wear tests under a 20 N load for 30 min, the wear rate of the coating prepared at 3000 W was 1.41 × 10(-4) mm(3)/(N·m), which is 13.5% lower than that of the 3200 W coating (1.63 × 10(-4) mm(3)/(N·m)) and 16.07% higher in wear resistance compared to the substrate. Cavitation erosion tests revealed that after 20 h of ultrasonic vibration, the mass loss of the 3000 W coating was only 2.35 mg, representing an 88.89% reduction compared to the substrate (21.15 mg), and significantly lower than that of the 3200 W (4.57 mg) and 3400 W (3.85 mg) coatings. This study demonstrates that precise control of laser power can effectively optimize the cavitation erosion resistance of high-entropy alloy coatings, providing technical support for their application in harsh environments.