Abstract
The objective was to evaluate the bending strength, phase transformation, roughness, and color stainability by coffee and red wine of opaque and high translucency yttria-stabilized zirconia before and after hydrothermal degradation in saline solution or oral mouthwash. Presintered zirconia blocks with medium opacity (ZrO(2)-3 mol. % of Y(2)O(3)) designed as ZrOp and high translucency zirconia (5.2 mol. % of Y(2)O(3)) designed as ZrTrans were used. Specimens (n = 80/group) were cut and sintered at 1500°C for 2 h. The specimens were hydrothermally degraded in an autoclave (134°C-1.8 kg/cm(2)) for 20 h in saline solution (0.5 g/L) and oral mouthwash solution (0.02% sodium fluoride, without alcohol and with 21.6% alcohol). After hydrothermal degradation, the samples were immersed in containers with coffee or red wine for 14 days to determine their color stainability. The results showed that the ZrOp had a higher bending strength than the ZrTrans before and after hydrothermal aging. In ZrOp and ZrTrans, the roughness increased after hydrothermal degradation. ZrOp samples had a higher Ra roughness than the ZrTrans samples. Roughness did not change after immersion in coffee or red wine. The X-ray diffraction (XRD) results showed that ZrOp samples underwent a tetragonal to monoclinic phase transformation, while ZrTrans samples were unchanged. Both ZrOp and ZrTrans samples changed color after immersion in coffee and red wine.