Abstract
High-performance batteries for military and extreme environment applications require alternatives to conventional liquid lithium-ion batteries (LIBs), which suffer from poor low-temperature performance and safety risks. All-solid-state lithium batteries (ASSLBs) offer enhanced safety and superior low-temperature capability. In this work, we designed and fabricated composite solid-state electrolytes using polyvinylidene fluoride (PVDF) and polyacrylic acid (PAA) as polymer matrices, N,N-dimethylformamide (DMF) as the solvent, and lithium bis(trifluoromethane sulfonimide) (LiTFSI) as the lithium salt. Composite solutions with varying PAA mass ratios were prepared. Advanced three-dimensional (3D) printing technology enabled the rapid and precise fabrication of electrolyte membranes. An ionic conductivity of about 2.71 × 10(-4) S cm(-1) at 25 °C, high mechanical strength, and good thermal properties can be achieved through component and 3D printing process optimization. Assembled LiCoO(2)||PVDF@PAA||Li ASSLBs delivered an initial discharge capacity of 165.3 mAh/g at 0.1 mA cm(-2) (room temperature), maintaining 98% capacity retention after 300 cycles. At 0 °C, these cells provided 157.4 mAh/g initial capacity with 85% retention over 100 cycles at 0.1 mA cm(-2). This work identifies the optimal PAA ratio for enhanced electrochemical performance and demonstrates the viability of 3D printing for advanced ASSLB manufacturing.