Evaluation of the patency rate and endothelialization of a poly-ε-caprolactone, nanofiber sheet-based vascular graft using a rat abdominal aortic implantation model

PCL grafts can exhibit autologous vessel-like regeneration; nonetheless, regarding patency, grafts made from rolled-up PCL nanofiber sheets have structural weaknesses. Further improvements are required to achieve a long-term and high patency rate for PCL grafts.

The PCL nanofiber sheets were created using an electrospinning machine. These nanofiber sheets were rolled up. Glue was applied between layers using a PCL solution to create a PCL nanofiber vascular graft, with an inner diameter of 1 mm. PCL grafts with 7 mm length were implanted into the abdominal aorta of rats. Thereafter, the patency was determined by pulsating blood flow from the hemiresection site of the distal aorta of the graft anastomosis, and endothelialization was examined using hematoxylin and eosin and immunofluorescent staining methods.

The patency rate of the PCL graft at 2 weeks was 57.1% (12 of 21 cases), which is not satisfactory as a small-caliber vascular graft. Patent cases, however, revealed a CD31-positive endothelial cell layer in the inner lumen and autologous cell infiltration into the scaffold, indicating autologous vessel-like regeneration. By contrast, the occluded cases showed disassembly of the nanofiber layers; and the inner layers folded into the middle of the lumen. This observation suggested that the disassembled inner layer of the PCL graft disturbed the blood flow and triggered occlusion. Conclusions: PCL grafts can exhibit autologous vessel-like regeneration; nonetheless, regarding patency, grafts made from rolled-up PCL nanofiber sheets have structural weaknesses. Further improvements are required to achieve a long-term and high patency rate for PCL grafts.