Abstract
This study aims to investigate the effect of hot deformation on commercially available Ti-6246 alloy below its β-transus transition temperature at 900 °C, knowing that the α → β transition temperature of Ti-6246 alloy is about 935 °C. The study systematically applies a thermomechanical processing cycle, including hot rolling at 900 °C and solution and ageing treatments at various temperatures, to investigate microstructural and mechanical alterations. The solution treatments are performed at temperatures of 800 °C, 900 °C and 1000 °C, i.e., below and above the β-transus transition temperature, for 9 min, followed by oil quenching. The ageing treatment is performed at 600 °C for 6 h, followed by air quenching. Employing various techniques, such as X-ray diffraction, scanning electron microscopy, optical microscopy, tensile strength and microhardness testing, the research identifies crucial changes in the alloy's constituent phases and morphology during thermomechanical processing. In solution treatment conditions, it was found that at temperatures of 800 °C and 900 °C, the α'-Ti martensite phase was generated in the primary α-Ti phase according to Burger's relation, but the recrystallization process was preferred at a temperature of 900 °C, while at a temperature of 1000 °C, the α″-Ti martensite phase was generated in the primary β-Ti phase according to Burger's relation. The ageing treatment conditions cause the α'-Ti/α″-Ti martensite phases to revert to their α-Ti/β-Ti primary phases. The mechanical properties, in terms of strength and ductility, underwent an important beneficial evolution when applying solution treatment, followed by ageing treatment, which provided an optimal mixture of strength and ductility. This paper provides engineers with the opportunity to understand the mechanical performance of Ti-6246 alloy under applied stresses and to improve its applications by designing highly efficient components, particularly military engine components, ultimately contributing to advances in technology and materials science.