Abstract
The present study effectively produced a high-entropy alloy (HEA) coating of AlCrFeMnNi on AISI 304L steel using resonant ultrasonic vibration-assisted laser cladding (R-UVALC). An investigation was conducted to examine the impact of dilution rate on the phase composition, microstructure, and mechanical and tribological properties of AlCrFeMnNi coatings. The coating, which was created utilizing the appropriate dilution rate, was thoroughly characterized using EDS mapping and TEM investigation. The results suggest that a higher dilution rate causes a change in the AlCrFeMnNi coating, transforming it from a single solid solution phase (BCC) into a two-phase solid solution containing both FCC and BCC phases. The analysis conducted using transmission electron microscopy (TEM) reveals that the AlCrFeMnNi coating, when diluted at an optimal rate of around 37%, is predominantly composed of a disordered body-centered cubic (BCC) phase and an ordered BCC (B2) phase featuring a spinodal decomposition structure. The AlCrFeMnNi coating has an average microhardness of approximately 540 HV, which is over 2.5 times higher than the microhardness of the substrate. Additionally, it was also established that the dilution rate has an impact on the occurrence of phases, which subsequently affects the mechanical and antifrictional properties of the coating. The integration of ultrasonic vibration in laser cladding enhances quality and improves mechanical and tribological properties, thereby reducing material costs and promoting an environmentally friendly process when compared to conventional cladding.