Abstract
The surface of calcined kaolinite particles underwent chemical modification using Vinyltriethoxysilane (VTMS) and 3-mercaptopropionic acid (3-MPA). The grafting ratio of VTMS on the calcined kaolinite surface was adjusted by varying its quantity. FT-IR analysis revealed the initial grafting of VTMS onto the kaolinite surface, resulting in the formation of a C=C reactive site on the surface. Subsequently, an olefin click reaction with 3-MPA occurred, leading to the effective grafting of 3-MPA onto the kaolinite surface and the formation of an efficient coating. Thermal analysis indicated that the optimal grafting level was achieved at a modifier content V:K ratio of 0.5. The estimated grafting ratio of the modifier on the kaolinite surface was approximately 40% when V:K was 0.5. Water contact angle and dispersion experiments demonstrated that the surface properties of kaolinite were effectively controlled by this modification approach. At V:K = 0.3, the modified kaolinite particles exhibited good dispersion in both polar and non-polar solvents. In polar solvents, the average particle size of modified kaolinite was below 1100 nm, while in non-polar solvents, it did not exceed 5000 nm. Considering all aspects, a V:K ratio of 0.3 is recommended. Further investigation into the impact of adding 3-MPA on the surface properties of modified kaolinite particles based on V:K = 0.3 revealed that the hydrophilicity of the modified particles could be enhanced. However, it is advised to keep the maximum M:V ratio (3-MPA to kaolinite) at 1.0.