Abstract
In this study, Al-Al4C3 compounds were manufactured by mechanical milling followed by heat treatment. To analyze the microstructural evolution, the composites were sintered at 550 °C at different sintering times of 2, 4 and 6 h. The mechanical results suggest that dislocation density and crystallite size primarily contribute to hardening before the sintering process, with a minimal contribution from particle dispersion in this condition. The compound exhibited a significant 75% increase in hardness after 2 h of sintering, primarily attributed to the nucleation and growth of Al4C3 nanorods. The HRTEM analysis, combined with geometric phase analysis (GPA) at and near the Al-Al4C3 interface of the nanorods, revealed strain field distributions primarily associated with partial screw dislocations and the presence of closely spaced dislocation dipoles. These findings are consistent with the microstructural parameters determined from X-ray diffraction pattern analysis using the convolutional multiple whole profile (CMWP) method. This analysis showed that the predominant dislocation character is primarily of the screw type, with the dislocation dipoles being closely correlated. Based on these results, it is suggested that samples with a lower weight percentage of reinforcement and longer sintering times may experience reduced brittleness in Al/Al4C3 composites. Strengthening contributions were calculated using the Langford-Cohen and Taylor equations.