Abstract
18Ni(300) maraging steel, which has exceptional strength and toughness, is used in the field of aviation and aerospace. In this paper, using a high-speed tribo-tester, tribological behaviors of 18Ni(300) maraging steel were investigated under high-speed dry sliding conditions. Morphology of the worn surfaces and the debris was analyzed by scanning electron microscope, and the oxides of worn surfaces caused by friction heat were detected by X-ray diffraction. The experiment results reveal that the friction coefficient of frictional pairs declines with increasing load and speed. With the speed and load increasing, oxides of the worn surfaces of 18Ni(300) maraging steel change from FeO to Fe(3)O(4) and the wear mechanism converts from adhesive wear into severe oxidative or extrusion wear.