Abstract
Based on the results achieved in systematic studies of structure formation and the formation of multicomponent phases, a scandium-containing filler metal from system alloy Mg-Zr-Nd for welding of aircraft casting was developed. The influence of scandium in magnesium filler alloy on its mechanical and special properties, such as long-term strength at elevated temperatures, was studied by the authors. It is established that modification of the magnesium alloy with scandium in an amount between 0.05 and 0.07% allows a fine-grained structure to be obtained, which increases its plasticity up to 70% and heat resistance up to 1.8 times due to the formation of complex intermetallic phases and the microalloying of the solid solution. Welding of the aircraft castings made of magnesium alloy with scandium-containing filler material allows obtaining a weld with a dense homogeneous fusion zone and the surrounding area without any defects. The developed filler material for welding surface defects (cracks, chips, etc.) formed during operation on aircraft engine bodies makes it possible to restore cast body parts and reuse them. The proposed filler material composition with an improved set of properties for the welding of body castings from Mg-Zr-Nd system alloy for aircraft engines makes it possible to increase their reliability and durability in general, extend the service life of aircraft engines, and obtain a significant economic effect.