Abstract
The purpose of this study is to investigate two new heat treatment processes on the mechanical properties of TC10 titanium alloy. By changing the β annealing temperature, the variation in microstructure and mechanical properties of TC10 titanium alloy were investigated. The results showed that with the increase in β annealing temperature the microstructure type changes from an equiaxed structure to a lamellar structure. The strength of the alloy then increases firstly, followed by a decrease, while the plasticity decreases all the time. Microstructure observation revealed that the alloy is uniformly composed of α phase and β phase after the two processes. In addition, it was found that the fracture morphology of the equiaxed structure is mainly dimples, showing ductile fracture characteristics, while the fracture morphology of lamellar microstructure is mainly crystalline, showing brittle fracture characteristics. These results indicated that reasonable β annealing temperature can be set according to different requirements to obtain different types of microstructure and mechanical properties, which expands the application field of TC10 titanium alloy.