Abstract
In this study, chopped natural bamboo fibers were successfully added in the benzoxazine matrix by the hot-pressing method to fabricate environmentally friendly bio-composite. The mechanical behaviors and failure mechanisms of neat benzoxazine matrix and its bamboo fiber composite under different tensile strain rates (quasi-static, 35/s and 110/s) were comparatively investigated using SHTB device (split-Hopkinson tensile bar), high-speed camera, DIC method (digital image correlation), and SEM observation (scanning electron microscopy). The results showed the composite exhibited 30.02% and 25.21% higher strength than that of neat benzoxazine under strain rates of 35/s and 110/s, respectively. However, under quasi-static tensile loading, the tensile strength of the composite was not higher than that of neat benzoxazine. The SEM and high-speed camera images showed the bamboo fibers displayed different reinforcing mechanisms under different strain rates. The chopped bamboo fibers could strengthen the composite effectively under dynamic tensile loadings. However, under quasi-static loading, the tensile strength of the composite was largely determined by the potential defects (such as small bubbles, pores, and fiber agglomerations) in the composite.