Abstract
In this study, some crucial parameters were determined of flexible polymer-organic solar cells prepared from an active layer blend of poly(3-hexylthiophene) (P3HT) and the fullerene derivative [6,6]-phenyl-C(61)-butyric acid methyl ester (PCBM) mixed in 1:1 mass ratio and deposited from chlorobenzene solution by spin-coating on poly(ethylene terephthalate) (PET)/ITO substrates. Additionally, the positive effect of an electron transport layer (ETL) prepared from zinc oxide nanoparticles (ZnO np) on flexible photovoltaic elements' performance and stability was investigated. Test devices with above normal architecture and silver back electrodes deposed by magnetron sputtering were constructed under environmental conditions. They were characterized by current-voltage (I-V) measurements, quantum efficiency, impedance spectroscopy, surface morphology, and time-degradation experiments. The control over morphology of active layer thin film was achieved by post-deposition thermal treatment at temperatures of 110-120 °C, which led to optimization of device morphology and electrical parameters. The impedance spectroscopy results of flexible photovoltaic elements were fitted using two R||CPE circuits in series. Polymer-organic solar cells prepared on plastic substrates showed comparable current-voltage characteristics and structural properties but need further device stability improvement according to traditionally constructed cells on glass substrates.