Abstract
Implant abutment connection was described among the main causes of peri-implant bone resorption. The aim of this in vitro study was to test the coupling capacity, the surface modification of a new hybrid connection and the influence of repeated connection activations caused during the main clinical and laboratory phases. A total of 40 implant-abutment screw retained systems with 10°-conical and internal hexagon connection were tested. The connection was screwed, fixed to the universal test machine, removed the screw and a pull-out test was performed. Test was repeated five times in succession. Also Scanning Electron Microscopy (SEM) was used to detect microscopically surface modification. Analysis of variance and Tukey tests were used for the statistical analysis. Pull-out test reveals a mean value of 131.35 ± 16.52 Newton Centimeter (N·cm). For each single activation, results from first to fifth were: 113.9 ± 13.02, 126.1 ± 12.81, 138.11 ± 15.15, 138.8 ± 11.90 and 140 ± 12.99 N·cm. A statistically significant difference between the measurements and an increase in the removal force was shown. The collected data supports the use of this new type of connection, resulting in a very strong interface between implant and abutment. Also, repeated activation of connection can promote a better coupling of the implant-abutment interface.