Abstract
: Printing technology offers a simple and cost-effective opportunity to develop all-printed stretchable circuits and electronic devices, possibly providing ubiquitous, low-cost, and flexible devices. To successfully prepare high-aspect-ratio Ag nanowires (NWs), we used water and anhydrous ethanol as the solvent and polyvinylpyrrolidone (PVP) as the viscosity regulator to obtain a water-soluble Ag NWs conductive ink with good printability. Flexible and stretchable fabric electrodes were directly fabricated through screen printing. After curing at room temperature, the sheet resistance of the Ag NW fabric electrode was 1.5 Ω/sq. Under a tensile strain of 0-80% and with 20% strains applied for 200 cycles, good conductivity was maintained, which was attributed to the inherent flexibility of the Ag NWs and the intrinsic structure of the interlocked texture.