Abstract
The development of MnO(2) as a cathode for aqueous zinc-ion batteries (AZIBs) is severely limited by the low intrinsic electrical conductivity and unstable crystal structure. Herein, a multifunctional modification strategy is proposed to construct N-doped KMn(8) O(16) with abundant oxygen vacancy and large specific surface area (named as N-KMO) through a facile one-step hydrothermal approach. The synergetic effects of N-doping, oxygen vacancy, and porous structure in N-KMO can effectively suppress the dissolution of manganese ions, and promote ion diffusion and electron conduction. As a result, the N-KMO cathode exhibits dramatically improved stability and reaction kinetics, superior to the pristine MnO(2) and MnO(2) with only oxygen vacancy. Remarkably, the N-KMO cathode delivers a high reversible capacity of 262 mAh g(-1) after 2500 cycles at 1 A g(-1) with a capacity retention of 91%. Simultaneously, the highest specific capacity can reach 298 mAh g(-1) at 0.1 A g(-1) . Theoretical calculations reveal that the oxygen vacancy and N-doping can improve the electrical conductivity of MnO(2) and thus account for the outstanding rate performance. Moreover, ex situ characterizations indicate that the energy storage mechanism of the N-KMO cathode is mainly a H(+) and Zn(2+) co-insertion/extraction process.