Abstract
This study investigates the resistive switching characteristics and underlying mechanism in 2D layered hexagonal boron nitride (h-BN) dielectric films using conductive atomic force microscopy. A combination of bipolar and threshold resistive switching is observed consistently on multi-layer h-BN/Cu stacks in the low power regime with current compliance (I (comp) ) of less than 100 nA. Standard random telegraph noise signatures were observed in the low resistance state (LRS), similar to the trends in oxygen vacancy-based RRAM devices. While h-BN appears to be a good candidate in terms of switching performance and endurance, it performs poorly in terms of retention lifetime due to the self-recovery of LRS state (similar to recovery of soft breakdown in oxide-based dielectrics) that is consistently observed at all locations without requiring any change in the voltage polarity for I (comp) ~1-100 nA.