Abstract
BACKGROUND: Dentures with antimicrobial properties are desirable for preventing Candida albicans adhesion. This study was to assess the effectiveness of bioactive glass (BAG) on C. albicans adhesion, surface roughness, and hardness of denture base materials. METHODS: Heat-polymerized (HP) and autopolymerized (AP) acrylic resins were used to fabricate 240 disk specimens (120/material, 60/C. albicans, 60/surface roughness and hardness). Specimens were divided into five groups (n = 10) based on the BAG concentration: 0.5, 1.5, 3, 5, and 7.5 wt% of the acrylic powder, with a control group comprised of unmodified specimens. Direct culture method was used to assess C. albicans adhesion. A profilometer and Vickers hardness test were used to measure surface roughness and hardness respectively. Analysis of variance (ANOVA) and post hoc Tukey's test were used for data analysis (α = 0.05). RESULTS: BAG addition significantly decreased the C. albicans count when compared with the control group (P < 0.001) for both HP and AP. Regarding surface roughness, there was no change in the HP acrylic resins (P > 0.05), while the AP acrylic resins exhibited significantly higher surface roughness with BAG addition (P < 0.001). The hardness of the HP and AP acrylic resins were significantly higher with the addition of BAG (P < 0.001). CONCLUSIONS: The addition of BAG to HP and AP acrylic resins effectively decreases C. albicans adhesion. The roughness of AP acrylic resins increases with the addition of BAG, while the hardness of both HP and AP acrylic resins increase with the addition of BAG.