Abstract
OBJECTIVES: To characterize two experimental zirconia bilayer materials compared to their monolithic controls, before and after hydrothermal aging. METHODS: Commercial zirconia powders were utilized to fabricate two bilayer materials: 3Y-TZP+ 5Y-PSZ (3Y+5Y/BI) and 4Y-PSZ+ 5Y-PSZ (4Y+5Y/BI), alongside control groups 3Y-TZP (3Y/C), 4Y-PSZ (4Y/C), and 5Y-PSZ (5Y/C). Compacted specimens were sintered (1550 °C- 2 h, 3 °C/min), and half of them underwent hydrothermal aging (134 °C-20h, 2.2 bar). Characterizations were performed through scanning-electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy, reflectance tests and biaxial flexural strength test (ISO:6872). Weibull statistics were applied to determine the characteristic strength and Weibull modulus. Grain size and optical properties were analyzed using two-way ANOVA followed by the Tukey test. RESULTS: Degradation regions and monoclinic phase were observed at aged 3Y-TZP and 4Y-PSZ surfaces. Significant differences were observed in the evaluation of optical properties between the bilayer and control groups. The bilayer materials presented intermediate characteristic strength values compared to their controls and aging significantly increased the strength of some groups. SIGNIFICANCE: Experimental bilayer materials presented lower mechanical properties than monolithic controls, 3Y/C and 4Y/C. Hydrothermal aging increased the characteristic strength of bilayered and monolithic controls, except for 5Y-PSZ. Both experimental bilayer systems, as well as monolithic controls, met the ISO 6872:2015 requirements for single-unit crowns (100 MPa), 3-unit fixed dental prostheses (FDPs) up to premolars (300 MPa), and 3-unit FDPs involving molars (500 MPa). However, for FDPs with four or more units, only monolithic 3Y-TZP and 4Y-PSZ, and bilayered 3Y+5Y met the required minimum flexural strength (≥800 MPa).