Abstract
Garnet oxide is one of the most promising solid electrolytes for solid-state lithium metal batteries. However, the traditional interface modification layers cannot completely block electron migrating from the current collector to the interior of the solid-state electrolyte, which promotes the penetration of lithium dendrites. In this work, a highly electron-blocking interlayer composed of potassium fluoride (KF) is deposited on garnet oxide Li6.4La3Zr1.4Ta0.6O12 (LLZTO). After reacting with melted lithium metal, KF in-situ transforms to KF/LiF interlayer, which can block the electron leakage and inhibit lithium dendrite growth. The Li symmetric cells using the interlayer show a long cycle life of ~3000 hours at 0.2 mA cm-2 and over 350 hours at 0.5 mA cm-2 respectively. Moreover, an ionic liquid of LiTFSI in C4mim-TFSI is screened to wet the LLZTO|LiNi0.8Co0.1Mn0.1O2 (NCM) positive electrode interfaces. The Li|KF-LLZTO | NCM cells present a specific capacity of 109.3 mAh g-1, long lifespan of 3500 cycles and capacity retention of 72.5% at 25 °C and 2 C (380 mA g-1) with an average coulombic efficiency of 99.99%. This work provides a simple and integrated strategy on high-performance quasi-solid-state lithium metal batteries.