Abstract
The effect of arc modes on the microstructure and tensile properties of 5183 aluminium alloy fabricated by cold metal transfer (CMT) processes has been thoroughly investigated. Heat inputs of CMT processes with three arc modes, i.e., CMT, CMT advance (CMT+A), and CMT pulse (CMT+P), were quantified, and their influence on the formation of pores were investigated. The highest tensile strength was found from samples built by the CMT+A process. This agrees well with their smallest average pore sizes. Average tensile strengths of CMT+A arc mode-built samples were 296.9 MPa and 291.8 MPa along the horizontal and vertical directions, respectively. The difference of tensile strength along the horizontal and vertical directions of the CMT+P and CMT samples was mainly caused by the pores at the interfaces between each deposited layer. The successfully built large 5183 aluminium parts by the CMT+A arc mode further proves that this arc mode is a suitable mode for manufacturing of 5183 aluminium alloy.