Abstract
In this paper, the characteristics of new porous coatings fabricated at three voltages in electrolytes based on H₃PO₄ with calcium nitrate tetrahydrate, magnesium nitrate hexahydrate, and copper(II) nitrate trihydrate are presented. The SEM, energy dispersive spectroscopy (EDS), glow discharge optical emission spectroscopy (GDOES), X-ray photoelectron spectroscopy (XPS), and XRD techniques for coating identification were used. It was found that the higher the plasma electrolytic oxidation (PEO) (micro arc oxidation (MAO)) voltage, the thicker the porous coating with higher amounts of built-in elements coming from the electrolyte and more amorphous phase with signals from crystalline Ca(H₂PO₄)₂∙H₂O and/or Ti(HPO₄)₂∙H₂O. Additionally, the external parts of the obtained porous coatings formed on titanium consisted mainly of Ti(4+), Ca(2+), Mg(2+) and PO₄(3-), HPO₄(2-), H₂PO₄(-), P₂O₇(4-) as well as Zn(2+) or copper Cu⁺/Cu(2+). The surface should be characterized by high biocompatibility, due to the presence of structures based on calcium and phosphates, and have bactericidal properties, due to the presence of zinc and copper ions. Furthermore, the addition of magnesium ions should accelerate the healing of postoperative wounds, which could lead to faster patient recovery.