Abstract
This paper presents a direct comparison of the mechanical and crack-healing properties of strain hardening cementitious composites (SHCC) under water submersion in a laboratory and in a natural environment outdoors. Portland cement, slag, crumb rubber powder, and hybrid polyethylene and polyvinyl alcohol fibers were used for the SHCC, and mixture proportions were determined. Specimens were exposed to different environmental conditions. A sequence of experimental tests including those for density, compressive strength, and tensile properties was performed to assess the mechanical properties of the SHCC. To confirm the healing feasibility of the SHCC, crack width reduction, stiffness recovery, and tensile performance at post-healing were adopted. The test results showed that underwater conditions are better than natural conditions in improving both the mechanical and crack-healing properties of SHCC. Specifically, the SHCC cured in natural conditions had a lower compressive strength, tensile strength, and tensile strain capacity than that cured in underwater conditions by 10%, 4%, and 3%, respectively. The SHCC cured in underwater conditions had a healing threshold of crack width of 60 µm, while the SHCC cured in natural conditions had very limited crack-healing capacity. Additionally, stiffness recovery of the SHCC cured in underwater conditions was higher than that cured in natural conditions.