Abstract
Isolating and observing the damage mechanisms associated with low-velocity impact in composites using traditional experiments can be challenging, due to damage process complexity and high strain rates. In this work, a new test method is presented that provides a means to study, in detail, the interaction of common impact damage mechanisms, namely delamination, matrix cracking, and delamination-migration, in a context less challenging than a real impact event. Carbon fiber reinforced polymer specimens containing a thin insert in one region were loaded in a biaxial-bending state of deformation. As a result, three-dimensional damage processes, involving delaminations at no more than three different interfaces that interact with one another via transverse matrix cracks, were observed and documented using ultrasonic testing and x-ray computed tomography. The data generated by the test is intended for use in numerical model validation. Simulations of this test are included in Part II of this paper.