Abstract
The aim of this research was to explore the use of a high-voltage electrical treatment (HVED) as a substitute for heating during the phosphorylation of maize starch. Starch was treated with HVED, phosphorylated with Na2HPO4 or Na5P3O10 with and without thermal treatment and phosphorylated in combination with HVED prior to and after the chemical modification. When starch was phosphorylated with Na2HPO4, HVED was more efficient in catalyzing reaction (3.89 mg P/kg for 30 min HVED in relation to 0.43 mg P/kg for thermal treatment), whereas with Na5P3O10 similar P content was achieved as with thermal treatment (0.76 P/kg for 30 min HVED in relation to 0.86 mg P/kg). The order of HVED and chemical reactions did not have a marked effect on phosphorous content. In combination with Na2HPO4, HVED pre-treatment had a more pronounced effect on the solubility and water absorption, whereas post-treatment was favoured with Na5P3O10. Mean diameter was increased by all treatments, where HVED had a marked effect. Enthalpy of gelatinization ranged from 11.76 J/g for starch treated with Na5P3O10 and 10 min-HVED to 13.58 J/g for Na5P3O10 treated sample. G' and G″ increased after both thermally and HVED enhanced phosphorylations, with a slightly more pronounced effect of the HVED.