Abstract
The Si/Al molar ratio of MAZ aluminosilicate zeolite prepared by the direct hydrothermal method is generally less than five, thus giving rise to poor thermal and hydrothermal stability for this low-silica zeolite. With the purpose of enhancing the Si/Al molar ratio of MAZ zeolite, post-synthesized methods including acetic acid treatment and steaming treatment, as well as interzeolite transformation from FAU zeolite, were employed to prepare MAZ zeolite with high silica. It was found that steaming treatment was more effective in increasing the Si/Al molar ratio in comparison with acetic acid treatment, affording a maximum Si/Al molar ratio of 16.9 along with a preserved crystallinity of approximately 75%. Additionally, high-silica MAZ zeolite with a Si/Al molar ratio of up to 7.3 was also capable of being directly hydrothermally synthesized using interzeolite transformation from FAU zeolite.