Abstract
The development of dental restorative materials with improved physical and mechanical properties is an important area of research. In this study, hexaallylaminocyclotriphosphazene (HAP) was used to modify dental composites. HAP is a compound with multiple carbon-carbon bonds that can react with methacrylic resins to form a copolymer. HAP was synthesized by reacting allylamine with hexachlorocyclotriphosphazene and characterized it using (1)H and (31)P NMR spectroscopy and MALDI-TOF mass spectrometry. Molecular dynamics simulations using the MM2 force field showed that HAP has a nanosize (the diameter of a sphere eclosing the molecule is 1.3 nm), making it a suitable nanomodifier for dental composites. Using 3D printing, samples of dental methacrylic composites containing up to 10 wt. % HAP were prepared and their physicomechanical properties and antibacterial activity against gram-positive bacteria S. mutans were studied. As a result, it was established that the maximum flexural strength (115.1 ± 10.2 MPa) is achieved with a modifier content of 5 wt.% in the composite. The maximum value of inhibition of S. mutans growth in a liquid nutrient medium is achieved with a HAP content of 10 wt.% in the sample. Furthermore, with a HAP content of more than 5 wt.% in the composite, inhibition of biofilm on the material surface is observed. The resulting composite is proposed for use as dental crowns in restorative dentistry.