Abstract
To address the brittle matrix failure frequently observed in filament-wound composite layers of onboard pressure vessels operating under cryogenic and high-pressure conditions, we studied a bisphenol-A epoxy resin (DGEBA) system modified with polyetheramine (T5000) and 3,4-Epoxycyclohexylmethyl 3',4'-epoxycyclohexanecarboxylate (CY179). The curing and rheological behavior of the modified resin were first evaluated, revealing a favorable processing, with viscosity suitable for wet-filament winding. Subsequently, its coefficient of thermal expansion (CTE) and tensile properties were characterized over the 300 K-90 K range, demonstrating a linear increase in elastic modulus and tensile strength with decreasing temperature. Carbon fibre-reinforced polymer composites (CFRP) were then fabricated using this resin system, and both longitudinal and transverse tensile tests, along with microscopic fracture surface analyses, were conducted. The results showed that CFRP-0° specimens exhibited an initial increase followed by a decrease in elastic modulus with decreasing temperature, whereas CFRP-90° specimens demonstrated pronounced cryogenic strengthening, with tensile strength and modulus enhanced by 52.2% and 82.4%, respectively. The findings provide comprehensive properties for the studied resin system and its CFRP under room temperature (RT) to cryogenic conditions, offering a basis for the design and engineering of cryo-compressed hydrogen storage vessels.