Abstract
The morphology of virgin reactor powder (RP) of high-density polyethylene (HDPE) with M(W) = 160,000 g/mol was investigated using DSC, SEM, SAXS, and WAXS methods. The morphological SEM analysis showed that the main morphological units of RP are macro- and micro-shish-kebab structures with significantly different geometric dimensions, as well as individual lamellae of folded chain crystals. A quantitative analysis of an asymmetric SAXS reflection made it possible to reveal the presence of several periodic morphoses in the RP with long periods ranging from 20 nm to 60 nm, and to correlate them with the observed powder morphology. According to the DSC crystallinity data, the thickness of the lamellae in each long period was estimated. Their surface energy was calculated in the framework of the Gibbs-Thompson theory. The presence of regular and irregular folds on the surface of different shish-kebab lamellae was discussed. The percentage of identified morphoses in the RP was calculated. It has been suggested that the specific structure of HDPE RP is due to the peculiarity of polymer crystallization during suspension synthesis in a quasi-stationary regime, in which local overheating and inhomogeneous distribution of shear stresses in a chemical reactor are possible.