Abstract
Zr-50Ti alloys are promising biomaterials due to their excellent mechanical properties and low magnetic susceptibility. However, Zr-50Ti alloys do not inherently bond well with bone. This study aims to enhance the bioactivity and bonding strength of Zr-50Ti alloys for orthopedic implant materials. Initially, the surface of Zr-50Ti alloys was treated with a sulfuric acid solution to create a microporous structure, increasing surface roughness and area. Subsequently, low crystalline calcium phosphate (L-CaP) precipitation was controlled by adding Mg(2+) and/or CO(3)(2-) ions in modified simulated body fluid (m-SBF). The treated Zr-50Ti alloys were then subjected to cold isostatic pressing to force m-SBF into the micropores, followed by incubation to allow L-CaP formation. The apatite-forming process was tested in simulated body fluid (SBF). The results demonstrated that the incorporation of Mg(2+) and/or CO(3)(2-) ions enabled the L-CaP to cover the entire surface of Zr-50Ti alloys within only one day. After short-term soaking in SBF, the L-CaP layer, modulated by Mg(2+) and/or CO(3)(2-) ions, formed a uniform hydroxyapatite (HA) coating on the surface of the Zr-50Ti alloys, showing potential for optimized bone integration. After soaking in SBF for 14 days, the bonding strength between the apatite layer and alloy has the potential to meet the orthopedic application requirement of 22 MPa. This study demonstrates an effective method to enhance the bioactivity and bonding strength of Zr-50Ti alloys for orthopedic applications.