Abstract
P(N-phenylmaleimide-alt-styrene) (P(NPMI-alt-St)) and P(N-(4-carboxyphenyl)maleimide-alt-styrene) (P(CPMI-alt-St)) were designed and synthesized via free radical copolymerization. Fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance spectroscopy (¹H NMR and 13C NMR), gel permeation chromatography (GPC), and differential scanning calorimetry (DSC) were used to confirm the structure of P(NPMI-alt-St) and P(CPMI-alt-St). Next, the effect of P(CPMI-alt-St) on the heat deflection temperature (HDT) of nylon 6 was studied. In comparison to the PA6/P(NPMI-alt-St) blend, with the addition of 10 wt %, the HDT value of the PA6/P(CPMI-alt-St) blend increased by 15.7 °C, and the glass transition temperature (Tg) by Dynamic mechanical analysis (DMA) increased 2.3 °C. According to the analysis of DMA, dynamic viscosity, and the SEM of PA6 and its blends, P(CPMI-alt-St) promoted its compatibility with PA6, and promoted the storage modulus and dynamic viscosity of the blends. Thus, the introduction of 4-carboxyl can significantly improve the effect of P(CPMI-alt-St) on the heat resistance modification of nylon 6.