Impact of different axial wall designs on the fracture strength and stress distribution of ceramic restorations in mandibular first molar

The

Under certain conditions, the occlusal distal veneer shows better performance than the full crown.

Forty human mandibular first molars were collected and randomized into four groups after establishing the distal defect: full crown group with 4 mm axial wall height (AWH) (FC4); short AWH crown group with 2 mm AWH (SC2); occlusal veneer group with 0 mm AWH (OV0); occlusal distal veneer group with only the distal surface prepared, and 4 mm AWH (OD4). The teeth were prepared according to the groups and the ceramic restorations were completed using celtra duo ceramic blocks. The ceramic thickness of the occlusal surface is about 1.5 mm and the edge is about 1 mm. The failure load values and fracture modes of each group were detected by mechanical test in vitro. According to the groups to establish three-dimensional finite element analysis (FEA) models, a 600 N loading force was applied vertically using a hemispherical indenter with a diameter of 6 mm. and compare the stress distribution under the condition of different restorations.

In vitro mechanical tests showed that the failure load values were SC2 (3232.80 ± 708.12 N) > OD4 (2886.90 ± 338.72 N) > VO0 (2133.20 ± 376.15 N) > FC4(1635.40 ± 413.05 N). The failure load values of the short AWH crown and occlusal distal veneer were significantly higher than that of occlusal veneer and full crown (P<0.05). The fracture modes of the full crown and occlusal veneer groups were mainly ceramic fractures and some were restorable tooth fractures. The short AWH crown and occlusal distal veneer groups presented with three fracture modes, the proportion of non-restorable tooth fracture was higher. The results of FEA show that under the spherical loading condition, the stress of ceramic was concentrated in the contact area of the loading head, the maximum von Mises stress values were FC4 (356.2 MPa) > VO0 (214.3 MPa) > OD4 (197.9 MPa) > SC2 (163.1 MPa). The stress of enamel was concentrated in the area where the remaining enamel was thinner, the maximum von Mises stress values was OD4 (246.2 MPa) ≈ FC4 (212.4 MPa) > VO0 (61.8 MPa) ≈ SC2 (45.81 MPa). The stress of dentin is concentrated in the root furcation and the upper third region of the root. However, stress concentration was observed at the tooth cervix in the full crown.