Abstract
This study systematically investigates the utilization of marble industry waste-waste marble powder (WMP) as partial cement replacement and waste marble aggregates (WMA) as partial fine aggregate replacement-in self-compacting concrete (SCC). A detailed experimental program evaluated the effects of various replacement levels (5%, 10%, and 20% for WMP; 20%, 30%, and 40% for WMA) on compressive strength and durability, particularly resistance to aggressive sulfuric acid environments. Results indicated that a 5% WMP replacement increased compressive strength by 4.9%, attributed primarily to the filler effect, whereas higher levels (10-20%) led to strength reductions due to limited pozzolanic activity and cement dilution. In contrast, WMA replacement consistently enhanced strength (maximum increase of 11.5% at 30% substitution) due to improved particle packing and aggregate-paste interface densification. Durability tests revealed significantly reduced compressive strength losses and mass loss in marble-containing mixtures compared to control samples, with optimal acid resistance observed at 20% WMP and 40% WMA replacements. A comprehensive life cycle assessment demonstrated notable reductions in environmental impacts, including up to 20% decreases in Global Warming Potential (GWP) at 20% WMP replacement. A desirability-based eco-cost-mechanical optimization-simultaneously integrating mechanical strength, environmental indicators, and production cost-identified the 10% WMP substitution mix as the most sustainable option, achieving optimal balance among key performance criteria. These findings underscore the significant potential for marble waste reuse in SCC, promoting environmental sustainability, resource efficiency, and improved concrete durability in chemically aggressive environments.