Abstract
The present study aims to investigate a Pd catalyst on a complex multi-oxide medium-entropy support interlayer La(2)O(3)-CeO(2)-ZrO(2)-Al(2)O(3) and its possible use as catalysts for methane abatement applications. The low-temperature N(2)-adsorption, XRD, TEM, XPS, TPD, and TPR techniques were used to characterize the catalyst. The palladium deposition on the supports leads to the formation of PdO. After the catalytic tests, the metal-Pd phase was observed. The complete oxidation of methane on Pd/La-Ce-Zr-Al catalyst takes place at temperatures above 250 °C, and in the presence of water vapor, the reaction temperature increases to about 70 °C. The careful choice of constituent oxides provides a balance between structural stability and flexibility. The alumina and lanthanum oxide ensure the high specific surface area, while the simultaneous presence of zirconia and ceria leads to the formation of a mixed-oxide phase able to interact with palladium ions by incorporating and de-incorporating them at different conditions. The mechanism of Mars-van Kerevelen was considered as the most probable for the reaction of complete methane oxidation. The possibility of the practical application of Pd-modified La-Ce-Zr-Al catalyst is evaluated. The use of a mix of multiple rare and abundant oxides makes the proposed catalyst a cost-effective alternative.