Abstract
Epoxy resins (ERs) are esteemed for their mechanical robustness and adhesive qualities, particularly in steel bridge deck applications. Nonetheless, their intrinsic brittleness limits broader utility. This study addresses this limitation by modulating ER crosslink density through adjustments in curing agent concentration, incorporation of hyperbranched polymers (HBPs), and optimization of curing conditions. Employing a multi-objective optimization strategy, this research aims to enhance toughness while minimizing strength degradation. Non-isothermal curing kinetics, realized using the differential scanning calorimetry (DSC) method, attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), tensile testing, and thermogravimetric analysis (TGA), were employed to investigate the effects of curing agent and HBP content on the curing reaction, mechanical properties, and thermal stability, respectively. Response surface methodology facilitated comprehensive optimization. Findings indicate that both curing agent and HBP contents significantly influence curing dynamics and mechanical performance. Curing agent content below 40% or above 50% can induce side reactions, adversely affecting properties. While a curing agent content exceeding 45% or an HBP content exceeding 5% improves the toughness of ER, these increases concurrently reduce mechanical strength and thermal stability. The study identifies an optimal formulation comprising 45.21% curing agent, a curing temperature of 60.45 °C, and 5.77% HBP content.