Abstract
This study investigates the synergistic effect of phenolic resin impregnation on the mechanical and adhesive properties of hydrothermally treated bamboo composites further reinforced with a silica nanoparticle sol-gel catalyzed by Fe(3)O(4) (SiO(2)/Fe(3)O(4)). The hydrothermal pre-treatment was found to enhance cellulose crystallinity, as confirmed through XRD analysis. Dynamic mechanical analysis (DMA) and nanoindentation tests revealed that the hybrid treatment significantly influences the viscoelastic response. Composites treated only with hot water and resin (GB-W) exhibited superior short-term creep resistance and higher elasticity, attributed to their optimized crystalline structure. In contrast, the silica-reinforced composites (GB-M) demonstrated the most viscous behavior and lowest stress relaxation, making them most effective at minimizing elastic springback. Nanoindentation further showed that GB-W had the highest nano-adherence at the fiber cell wall level. FTIR analysis indicated a stronger interaction between the phenolic resin and the hydroxyl groups of the bamboo matrix in GB-0 and GB-W compared to GB-M, where the silica layer potentially altered this interface. Microscopy confirmed a resin penetration depth of at least 1 mm, primarily into porous tissues. The results demonstrate that while silica reinforcement enhances relaxation properties, the hydrothermal pre-treatment combined with phenolic resin creates a more favorable interface, leading to better overall creep resistance and adherence.