Abstract
Waterborne polyurethane cationomer coatings modified with 1,3-bis(3(3-(propoxy-2-ol-)-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide)-3-propyloxy))tetramethyldisiloxane (TMDS-AGE-DOPA) containing phosphorus and silicon atoms were obtained. Their structures were confirmed by Fourier transform infrared (FTIR) spectroscopy. The effect of TMDS-AGE-DOPA on thermal properties, flame retardancy, and surface characteristics (gloss, contact angle, surface free energy), as well as performance properties (hardness, impact resistance), was investigated. A coupled TG-FTIR technique was employed for evolved gas analysis. Thermal stability decreased with the addition of the modifier, while the glass transition temperature increased from -19 to 25 °C. The modifier improved the flame retardancy of the material by shifting the peak temperature of the heat release rate (T(PHRR)) to lower values. The gloss of the coatings was very high (>90 GU at all angles studied), although it decreased with increasing modifier content. The presence of phosphorus moieties from the modifier enhanced hydrophilicity, raising surface free energy (SFE) from 37.9 to 44.0 mJ/m(2). The coatings are soft materials with a Persoz hardness in the range of 0.05-0.32. The modifier increased hardness but reduced impact strength. The obtained cationomers can be applied as environmentally friendly coatings on hydrophilic surfaces such as textiles, glass, or wood.