Abstract
This study developed a full solid waste-based cementitious material (ISWs-CM) using steel slag (SS), ground granulated blast furnace slag (GGBFS), phosphorus slag (PS), carbide slag (CS), and desulfurized gypsum (DG) to completely replace cement. A two-layer optimization strategy, combining three chemical moduli and simplex lattice experiments, was employed to determine the proportion and to investigate the impact of proportions on the uniaxial compressive strength of mortar. As an application case, the ISWs-CM with the optimal proportion was employed to stabilize aeolian sand, and its effectiveness as a cement substitute and the underlying mechanisms were investigated. The results indicated that the ISW proportion that maximized the strength of the mortar was SS:GGBFS:PS:CS = 5:20:20:40. The strength of the mortar was enhanced when the proportion of GGBFS exhibiting the highest reactivity was increased and also increased initially and then decreased with an increase in CS when the dosage of GGBFS was fixed. The aeolian sand stabilized by ISW-CM exhibited higher strength than that stabilized with cement. The greater number and variety of hydration products resulted in denser connections and encapsulation of sand particles, which highlights the synergistic effect of ISWs and the potential of ISW-CM as a cement replacement across diverse applications including aeolian sand stabilization.